Product Introduction
Model number
item
SG 3288
SG 3299
use
Hardwood special glue: integrated wood board, high-end furniture solid wood
Solid wood panel, finger joint, solid wood floor composite, high-end furniture
Bonding of non-structural integrated wood, such as cold pressing of solid wood floor
Solid wood panels and integrated wood gluing, high frequency panels, etc
Two components, fast curing speed, high bonding strength, use
High initial strength, water resistance, solvent resistance, suitable for oak, pomelo
peculiarity
Especially suitable for oak, ash, oak, teak,
Suitable for most hardwoods under specified curing agent and environment,
Wood, ash, beech, rubber wood, lotus, pine and so on
And all kinds of hardwood cold pressed veneer
Acacia wood, yoke wood and other common medium hardwood resistance to water and heat
Multiple types of wood bonding
name
SG 3288
SG 3299
appearance
Milky liquid
Milky liquid
viscosity
10000-16000 cps(25℃)
9500-11000 cps (25℃)
Solid content
48 to 52%
48 to 52%
Host agent
PH
7-8 -
7-8 -
Specific gravity
1.2 + / - 0.1
1.2 + / - 0.1
Standard packing
20kg/ barrel, 25kg/ barrel, 50kg/ barrel, 1000kg/ barrel,
Lay by
The storage period is 6 months at room temperature, and the increase of room temperature will shorten the storage period. Winter storage temperature should not be lower than 8℃ to prevent freezing
name
Curing agent
Curing agent
appearance
Light dark yellowish-brown liquid
Dark brown liquid
Curing agent
viscosity
< 0.2Pa.s (25°C)
Standard packing
250kg/ barrel, 10kg/ barrel, 3kg/ barrel.
Lay by
Store at room temperature and fully sealed for 12 months
Ratio of main agent and curing agent
Main agent: Curing agent =100:15(weight ratio)
Main agent: Curing agent =100:13-15(weight ratio)
Active period
35-50 minutes (20-25℃)
-- One
Glue spread
180-220 g/m
180-240 g/m
Moisture content of wood
8-12%
8-12%
Usage parameters (examples)
Curing temperature
> 20 ℃
> 10 ℃
Pressure time
120-180 minutes
Cold pressing 120-150 minutes High frequency :180-300 seconds
Compression pressure
10-15 kg/cm
8-15 kg/cm²
Age after pressure relief
24-72 hours
24-72 hours
item
SG 3288
SG 3299
use
Hardwood special glue: integrated wood board, high-end furniture solid wood
Solid wood panel, finger joint, solid wood floor composite, high-end furniture
Bonding of non-structural integrated wood, such as cold pressing of solid wood floor
Solid wood panels and integrated wood gluing, high frequency panels, etc
Two components, fast curing speed, high bonding strength, use
High initial strength, water resistance, solvent resistance, suitable for oak, pomelo
peculiarity
Especially suitable for oak, ash, oak, teak,
Suitable for most hardwoods under specified curing agent and environment,
Wood, ash, beech, rubber wood, lotus, pine and so on
And all kinds of hardwood cold pressed veneer
Acacia wood, yoke wood and other common medium hardwood resistance to water and heat
Multiple types of wood bonding
name
SG 3288
SG 3299
appearance
Milky liquid
Milky liquid
viscosity
10000-16000 cps(25℃)
9500-11000 cps (25℃)
Solid content
48 to 52%
48 to 52%
Host agent
PH
7-8 -
7-8 -
Specific gravity
1.2 + / - 0.1
1.2 + / - 0.1
Standard packing
20kg/ barrel, 25kg/ barrel, 50kg/ barrel, 1000kg/ barrel,
Lay by
The storage period is 6 months at room temperature, and the increase of room temperature will shorten the storage period. Winter storage temperature should not be lower than 8℃ to prevent freezing
name
Curing agent
Curing agent
appearance
Light dark yellowish-brown liquid
Dark brown liquid
Curing agent
viscosity
< 0.2Pa.s (25°C)
Standard packing
250kg/ barrel, 10kg/ barrel, 3kg/ barrel.
Lay by
Store at room temperature and fully sealed for 12 months
Ratio of main agent and curing agent
Main agent: Curing agent =100:15(weight ratio)
Main agent: Curing agent =100:13-15(weight ratio)
Active period
35-50 minutes (20-25℃)
-- One
Glue spread
180-220 g/m
180-240 g/m
Moisture content of wood
8-12%
8-12%
Usage parameters (examples)
Curing temperature
> 20 ℃
> 10 ℃
Pressure time
120-180 minutes
Cold pressing 120-150 minutes High frequency :180-300 seconds
Compression pressure
10-15 kg/cm
8-15 kg/cm²
Age after pressure relief
24-72 hours
24-72 hours